Flexible substrates containing a radiation curable coating composition

ABSTRACT

A radiation curable coating comprising: A. an oligomer of Formula I: &lt;IMAGE&gt;  (I)   wherein: R1 is hydrogen or methyl; Y is a divalent urethane residue; B. an acrylic ultra-violet light absorber of Formula IV:    &lt;IMAGE&gt; (IV)   wherein R4 is alkyl or hydroxy alkylene. Preferably the coating composition contains a vinyl monomer copolymerizable with the oligomer. The process for curing the coating is also disclosed.

This is a division of application Ser. No. 865,663, filed Dec. 29, 1977 now U.S. Pat. No. 4,129,667.

CROSS REFERENCE TO RELATED APPLICATION

(a) U.S. application Ser. No. 865,664 filed concurrently with this application now U.S. Pat. No. 4,135,007 disclosing and claiming different but related subject matter.

(b) Commonly assigned U.S. application Serial Number 865,665 filed concurrently with this application now abandoned disclosing and claiming certain novel ultra-violet light absorbers useful in the present invention.

Coating compositions which are curable under the influence of radiation in general and ultra-violet light as well as electron beam in particular are well known. Representative examples of prior coating compositions include those disclosed in U.S. Pat. Nos. 3,782,961; 3,829,531; 3,850,770; 3,874,906; 3,864,133; 3,891,523; 3,895,171; 3,899,611; 3,907,574; 3,912,516; 3,932,356; and 3,989,609. Unfortunately, these coating compositions suffer from a number of disadvantages and do not have an in situ ultra-violet absorber in the composition. Many of these coating compositions have insufficient flexibility that causes them to crack when applied to flexible substrates such as those of polyvinyl chloride. Other compositions do not adhere sufficiently to the substrate with the undesirable result that they become dislodged or peel. Still other coating compositions require the use of solvents that must be evaporated during the curing process. The evaporation of such solvents consumes energy and creates atmospheric pollution problems. Other compositions produce coatings that yellow, do not weather well, and have insufficient scratch-resistance, stain-resistance, abrasion-resistance, and/or solvent-resistance.

The use of ultra-violet absorbers in plastics or coatings to enhance weather resistance is known. The absorbers absorb the radiation and dissipate the energy and thus protect the coating from structural degradation. Considerable economic saving is realized by incorporating the ultra-violet absorber on the surface of a plastic article rather than using the ultra-violet absorber in conventional bulk application. Conventional surface application, such as the use of a solvent or paint vehicle is, moreover, undesirable in view of the pollution hazard and bulk handling procedures. Radiation curing has made possible production of coating films which are easier to handle, but heretofore ultra-violet absorbers have consumed the energy from the radiation source resulting in too high energy demands in curing or too slow curing rates. If a small amount of ultra-violet photoinitiator is used to facilitate curing, then addition of use levels of most ultra-violet stabilizers would prevent the curing from occurring.

Accordingly it is an object of the present invention to provide an improved coating composition that is substantially free of one or more of the disadvantages of prior radiation curable coating compositions.

Yet another object is to provide a coating composition that will produce a coating that is weather-resistant, non-yellowing, scratch-resistant, stain-resistant, abrasion-resistant, and solvent-resistant.

Yet another object is to provide a coating composition that is free of volatile solvents.

Another object is to provide an improved process for coating substrates such as those of natural leather, synthetic leather, polyvinyl chloride, polyurethanes, and polycarbonates.

Still another object is to provide a coating composition with an ultra-violet absorber which can be cured by radiation.

Other objects and advantages of the present invention will be apparent to those skilled in the art by reference to the following detailed description.

FIG. 1 is a graph of light transmission of polyvinyl chloride (hereinafter PVC) glazing.

FIG. 2 is a graph of yellowness index of PVC glazing.

FIG. 3 is a graph of light transmission of PVC glazing wherein the coating with ultra-violet absorber has different thicknesses. The coating is UV cured.

FIG. 4 is a graph of yellowness index of PVC glazing coated with a composition containing an ultra-violet absorber and of different thicknesses. The coating is UV cured.

FIG. 5 is a graph of the light transmission of PVC coated with ultra-violet absorbers. The coating is electron beam cured.

FIG. 6 is a graph of yellowness index of PVC glazing with a coating containing ultra-violet absorbers. The coating is electron beam cured.

FIG. 7 is a graph of yellowness index of polycarbonate glazing with a coating containing a hydroxyethyl-2-cyano-3,3' diphenyl acrylate ultra-violet absorber. The coating is UV cured.

The above and other objects are accomplished according to the present invention by providing a coating composition comprising:

A. an oligomer of Formula I: ##STR3## wherein: R¹ is hydrogen or methyl;

Y is a divalent urethane residue;

B. an acrylic ultra-violet light absorber of Formula IV: ##STR4## wherein R⁴ is alkyl or hydroxy alkylene. Preferably a vinyl monomer or monomers are included which are copolymerizable with the oligomer. Oligomers of Formula I with an acrylic or methacrylic component are well known in the art. Oligomers of this type are shown in U.S. Pat. Nos. 3,907,574; 3,874,906; 3,989,609; and 3,895,171. A preferred type of oligomer contains both an acrylic component and a urethane portion in the Y radical. Examples of these compounds are found in U.S. Pat. Nos. 3,912,516; 3,891,523; 3,864,133; and 3,850,770.

Preferred novel types of acryl urethane are shown by Formulas II and III: ##STR5## wherein: R¹ is hydrogen or methyl;

R² is lower alkylene;

R³ is aliphatic or cycloaliphatic;

X is --O-- or --NH--;

n is an integer from 2 to 50 inclusive.

These oligomers are produced by reacting polytetrahydrofuran, polycaprolactone polyols and other polyols with a diisocyanate to produce an isocyanate terminated prepolymer. The isocyanate terminated prepolymer is then capped with a capping agent to produce the oligomer of Formula II and Formula III. The preferred oligomers of Formula II are those of Formula V and the preferred oligomers of Formula III are those of Formula VI: ##STR6## wherein "n" is an integer from 5 to 20 inclusive.

The polytetrahydrofuran is commercially available from the Du Pont Company under the tradenames "TERRECOL-650", "TERRECOL-1000", and "TERRECOL-2000", and from the Quaker Oats Company under the tradenames "POLYMEG-650", "POLYMEG-1000", and "POLYMEG-2000". In the above tradenames the number indicates the approximate molecular weight of the polytetrahydrofuran. The most preferred polytetrahydrofuran is that having a molecular weight of 650 which is consistent with the definition of "n" in Formulas II and V herein. At higher molecular weights wherein "n" exceeds about 50 the resultant oligomer has too high a viscosity.

The caprolactone polyols are commercially available from Union Carbide Corp. under the tradenames "NIAX CAPROLACTONE POLYOLS" -PCP-0200, PCP-0210, PCP-0230, PCP-0240, PCP-0300, PCP-0301 and PCP-0310. The 0200 series are diols with molecular weights 530, 830, 1250 and 2000 respectively. The 0300 series are triols with molecular weights 540, 300 and 900 respectively.

The oligomers of Formula II, III, V, and VI can be produced in accordance with U.S. Patent application, Ser. No. 777,031 filed Mar. 4, 1977 now U.S. Pat. No. 4,129,709. The capping agents useful in the present invention are those that will react with the isocyanate terminated prepolymer to produce the oligomers of Formula II. In general, any capping agent having a terminal amine or hydroxyl group and also having an acrylic acid or methacrylic acid moiety is suitable. Examples of suitable capping agents include among others hydroxyethyl acrylate, hydroxyethyl methacrylate, hydroxypropyl acrylate, hydroxypropyl methacrylate, hydroxybutyl acrylate, hydroxybutyl methacrylate, hydroxypentyl acrylate, hydroxypentyl methacrylate, hydroxyhexyl acrylate, hydroxyhexyl methacrylate, aminoethyl acrylate, and aminoethyl methacrylate.

The diisocyanates useful to produce oligomers of Formula II are aliphatic and cycloaliphatic diisocyanates that will react with terminal hydroxyl groups present on the polytetrahydrofuran. Of course, aromatic diisocyanates undergo the same reaction but do not yield a product as satisfactory as that obtained by the use of aliphatic diisocyanates. Examples of suitable diisocyanates include among others, isophorone diisocyanate, 4,4'-dicyclohexylmethane-diisocyanate available commercially from the Du Pont Company under the trade name "Hylene W", and trimethyl-hexamethylene-diisocyanate, 1,6 hexamethylene diisocyanate, 2,4,4 trimethyl 1,6 hexylene diisocyanate, octadecylene diisocyanate and 1,4 cyclohexylene diisocyanate. The preferred diisocyanates are isophorone diisocyanate (3-isocyanatomethyl 3,5,5 trimethyl cyclohexyl isocyanate) and 4,4' dicyclohexylmethane-diisocyanate.

The vinyl monomer copolymerizable with the oligomer may be one or more monomers compatible with the oligomer selected. N-vinyl-2 pyrrolidone and acrylic acid esters having a boiling point of at least 200° C. at 760 mm Hg are preferred. These monomers allow adjustment of the viscosity for ease of coating operations and N-vinyl-2-pyrrolidones also enhance the rate of curing.

The weight ratio of oligomer to N-vinyl-2-pyrrolidone can vary widely as long as the properties of the resultant cured coating composition are not adversely affected, however, they are generally present in a weight ratio of 1:9 to 9:1 and preferably 1:3 and 3:1. At higher ratios, e.g., those rich in oligomer, the uncured coating composition tends to have too high a viscosity. This high viscosity makes it difficult to apply the uncured coating composition to the substrate. At lower ratios the resultant cured coating composition tends to be too hard and inflexible.

The acrylic acid ester should have a boiling point of at least 200° C. at 760 mm Hg. Acrylic acid esters of lower boiling points tend to vaporize during curing. Such vaporization causes undesirable changes in the coating composition. Furthermore, vaporized acrylic acid esters tend to polymerize on the radiation source, e.g., ultra-violet lamps or electron beam window. This vaporization also causes undesirable atmospheric pollution. The acrylic acid esters useful in the present invention include, among others, monoesters, diesters and higher esters of both acrylic acid and methacrylic acid. Examples of suitable acrylic acid esters include, among others, 1,4-butanedioldiacrylate, 1,6-hexanedioldiacrylate, neopentylglycoldiacrylate, pentaerythritol-tetramethacrylate, trimethylolpropane-triacrylate, ethylhexyl-acrylate, ethylhexylmethacrylate, pentyl-acrylate, hexyl-acrylate, and cyclohexylmethacrylate. 1,4-butanedioldiacrylate and 1,6 hexanedioldiacrylate are the preferred acrylic acid esters.

The acrylic acid ester can be present in the coating composition in widely varying amounts but is generally present in a weight ratio of 1:9 to 9:1 and preferably 1:3 to 3:1 compared to the oligomer of Formula I or II.

The acrylic ultra-violet light absorber is of Formula IV: ##STR7## wherein R⁴ is alkyl or hydroxyalkyl. The R⁴ group may be methyl, ethyl, propyl, iso-propyl, butyl, pentyl, hexyl, octyl, etc. Alkyl groups with 1 to 12 carbon atoms, and preferably 1-8 carbon atoms are used. The compounds are referred to as Uvinuls. If the R⁴ is an ethyl group, the compound is designated N-35, i.e., ethyl-2-cyano-3,3-diphenyl acrylate. If R⁴ is ethylhexyl the compound is designated N-539, i.e., 2-ethylhexyl-2-cyano-3,3-diphenyl acrylate. These compounds are available commercially from General Aniline and Film Corp. If R⁴ is hydroxyethylene the compound is hydroxyethyl 2-cyano-3,3-diphenyl acrylate, an experimental product of GAF. The synthesis of this product is given in Examples 1 to 3 of Reference (b).

The amount of ultra-violet absorber of the above formula in the coating compositions for radiation curing can vary from 0.5 to 3%. Lesser amounts do not give a coating that retains the light transmission or low yellowness of the coating. Greater amounts retard the curing to an unacceptable level.

If the curing is done with ultra-violet light a photo-initiator is used. Suitable photo-initiators include vicinal ketaldonyl compounds (i.e., compounds containing a ketone group and an aldehyde group) such as diacetyl, benzil; 2,3-pentanedione, 2,3-octanedione, 1-phenyl-1,2-butanedione, 2,2-dimethyl-4-phenyl-3,4-butanedione, phenyl-glyoxal, diphenyl-triketone; aromatic diketones, such as anthraquinone; acyloins, such as benzoin; pivaloin acryloin ethers, such as benzoin-methyl-ether, benzoin-ethyl-ether, benzoin-butyl-ether, benzoin-isobutyl-ether, benzoin-phenyl-ether; alpha-hydrocarbon substituted aromatic acyloins, including alpha-methyl-methylbenzoin, alpha-alkyl-benzoin, as in U.S. Pat. No. 2,722,512, and phenylbenzoin; diaryl ketones, such as benzophenone and dinaphthyl ketone; and organic disulfides, such as diphenyldisulfide. The photo-initiator can also include a synergistic agent, such as a tertiary amine, to enhance the conversion of photo-absorbed energy to polymerization initiating free radicals. Diethoxyacetophenone available from Union Carbide Corp., dimethoxyphenylacetophenone such as IRGACURE 651 available from Ciba-Geigy or a benzoin either such as Vicure 10 available from Stauffer Chemical Co. are preferred. The photo-initiator is present in the coating composition in an amount sufficient to initiate the desired polymerization under the influence of the amount of actinic light energy absorbed. The coating composition generally contains from 0.01 to 5 weight percent of photo-initiator based on the weight of the coating composition.

The coating composition can also contain an addition polymerization inhibitor to prevent undesirable auto-polymerization of the coating composition in storage prior to use. Examples of suitable addition polymerization inhibitors include, among others, di(1,4 secbutylamino) benzene available from the Du Pont Company under the trade name "Anti-Oxidant 22" and phenothiazine available from Tefenco Chemical Co. The addition polymerization inhibitor is present in an amount sufficient to prevent auto-polymerization and is generally present in an amount from 100-300 PPM based on the weight of the coating composition.

The coating composition can also contain a surfactant. The preferred surfactants are silicone surfactants such as that available from the Dow Corning Corporation under the trade name "DC-193". The surfactant is present in an amount necessary to reduce the surface tension of the coating composition and reduce its viscosity to the desired level. The surfactant generally comprises from 0.1 to 5 weight percent based on the weight of the coating composition.

The coating compositions of the present invention can also contain other conventional additives, such as flow control and leveling agents, organic and inorganic dyestuffs and pigments, fillers, plasticizers, lubricants, and reinforcing agents, such as alumina, silica, clay, talc, powdered glass, carbon black and fiberglass.

The coating compositions of the present invention can be cured by applying them as a film 0.5 mil thick on the substrate. Curing is preferably done under an inert atmosphere of nitrogen. The coating composition may be applied as a thin film in any conventional manner such as by spraying, brushing, dipping, roll coating and the like.

Conventionally, the film on the substrate is positioned to travel on a conveyor and pass under a source of a free radical generator, such as radiation. The coated side of the substrate is exposed to the radiation for a time sufficient to effect polymerization and convert the film into an adherent, tough, flexible coating.

As used herein the term radiation refers to any radiation source which will produce free radicals and induce addition polymerization of vinyl bonds. The actinic radiation is suitably in the wave length of 2000-7500 A, preferably 2000 to 4000. A class of actinic light useful herein is ultra-violet light and other forms of actinic radiation are from the sun, artificial sources such as Type RS sunlamps, carbon arc lamps, Xenon arc lamps, mercury vapor lamps, tungsten halide lamps, lasers, fluorescent lamps with ultra-violet light emitting phosphors.

Ultra-violet curing rates greater than 20 ft/min/lamp must be obtained in order to be commercially acceptable. With a reasonable thickness (less than 10 mils) coating the coating compositions with the ultra-violet absorber of Formula IV, present in an amount from 0.5 to 3% based on the weight of the composition, can be cured at rates of 25-50 ft/min/lamp.

The preferred electron beam system contains a wide curtain of electrons directly from a linear cathode. A curtain of electrons from the gun's cathode, accelerated to a high velocity by a 200 KV potential, emerges from the chamber through a foil window into the coated substrates (Electroncurtain™ by Energy Sciences, Inc.).

The electron beam curing of the coating compositions as described above is cured at less than 5 Mrads and generally at 2 Mrads. Curing at greater than 8 Mrads is deemed unacceptable because of the high cost.

Laminates of film coatings based on acryl urethanes with an ultra-violet absorber of hydroxy alkylene cyano diphenylacrylate applied on clear polycarbonate are surprisingly non-leachable and do not yellow.

The invention is further illustrated by the following examples in which all parts and percentages are by weight unless otherwise indicated. These non-limiting examples are illustrative of certain embodiments designed to teach those skilled in the art how to practice the invention and to represent the best mode contemplated for carrying out the invention.

The following abbreviations are used in the following examples and tables:

THF: polytetrahydrofuran

NP- N-vinyl-2 pyrrolidone

B,DDA: 1,4 butanedioldiacrylate

IPDI- isophorone diisocyanate

TMDI: trimethyl hexamethylene diisocyanate

Hylene W: 4,4' dicyclohexylmethane diisocyanate

HEA: hydroxyethyl acrylate

HEMA: hydroxyethyl methacrylate

N-35: ethyl-2-cyano-3,3-diphenyl acrylate

N-539: ethylhexyl-2-cyano-3,3-diphenyl acrylate

HECDA: hydroxyethyl 2-cyano-3,3-diphenyl acrylate

PCP: polycaprolactone polyol

EXAMPLE 1

This example is illustrative of forming the inventive coating composition based on THF/IPDI/HEA Oligomer. The quantities of the following items were combined as indicated below:

    ______________________________________                                                       QUANTITY                                                         ITEM       NAME     (gms)    (mols)                                            ______________________________________                                         A         THF       356      0.55                                              B         NP        173.3    1.56                                              C         B,DDA     121.7    0.61                                              D         IPDI      267      1.20                                              E         HEA       139      1.20                                              F         N-35      31.7            3%                                         ______________________________________                                    

The following procedure was used: The reaction is carried out under dry air. Items B, C and D are added to a reactor equipped with a mechanical stirrer, a reflux condenser and two separatory funnels. Phenothiazine (0.06 g) is added. This mixture is agitated vigorously at a temperature of 45° C. At this point, 2.4 ml. of a 10 weight percent solution of catalyst of dibutyl tin dilaurate in ethylhexyl acrylate is injected. The temperature is raised to 50°±2° C. and Item A is added dropwise from a separatory funnel. This addition takes approximately 40 min. Another 1.6 ml. of the catalyst is then injected and the temperature is raised to 56°±2° C., where it is kept for 2 hours. The temperature of the reaction mixture is lowered to 50°±2° C. and Item E is added dropwise from the other funnel. The addition takes about 45 min. to complete. The temperature is raised to 56°±2° C. where it is kept for 3 hours. At the end of the reaction Item F (3% on the product weight) is mixed in. Silicone oil may be added. The product is stored in an amber glass bottle at the ambient temperature. For electron beam curing, the product is ready for use. For ultra-violet light curing, a photo-initiator is added and mixed well before use.

EXAMPLES 2-4

These examples are illustrative of forming the inventive coating compositions. Table I shows the amounts of ingredients combined in the examples. The procedure of Example 1 was followed substituting the specified amounts of ingredients as shown in Table I. The amounts of ingredients in Example 1 are also shown in Table I for convenience.

                                      TABLE I                                      __________________________________________________________________________            1      2         3         4                                            EXAMPLE                                                                               Parts                                                                              Mols                                                                              Parts  Mols                                                                              Parts  Mols                                                                              Parts Mols                                   __________________________________________________________________________     THF    356 0.55                                                                              356    0.55                                                                              356    0.55                                                                              356   0.55                                   NV     173.3                                                                              1.56                                                                              186.3  1.68                                                                              190.3  1.71                                                                              172.1 1.55                                   B,DDA  121.7                                                                              0.61                                                                              128.6  0.65                                                                              131.6  0.66                                                                              119.5 0.60                                   diisocyanate                                                                          267 1.20                                                                              315    1.20                                                                              315    1.20                                                                              253   1.20                                          (IPDI) (Hylene W)                                                                               (Hylene W)                                                                               (TMDI)                                       capping agent                                                                         139 1.20                                                                              139    1.20                                                                              156    1.20                                                                              139   1.20                                          (HEA)  (HEA)     (HEMA)    (HEA)                                        u-v absorber                                                                          31.7   33.7      34.5      31.2                                                (N-35) (N-35)    (N-35)    (N-35)                                       __________________________________________________________________________

EXAMPLE 5

This example illustrates the synthesis of a coating composition of the present invention employing two acrylic acid esters.

The procedure of Example 1 is repeated employing the same times, conditions and ingredients except that one-half the quantity of mols of the B,DDA is replaced with ethylhexylacrylate with similar results.

EXAMPLE 6

This example illustrates applying the inventive coating composition to a vinyl sheet. To the composition of Example 4 is added 2% of a benzoin ether (Vicure 10 available from Stauffer Chemical) and a 1-mil thick film is applied on a vinyl sheet. The coated vinyl sheet is cured by passing through a PPG QC Lab UV oven containing two 200 w/in. UV lamps at a speed of 100 ft/min/2 lamps. No solvent was left after the cure. The coating is dry, flexible, scratch-resistant, strain-resistant, abrasion-resistant, and solvent-resistant. The curing rate is 75 ft/min/2 lamps.

The product has been shown to give coatings with good hand on fabrics. The elongation of the cured film is in the order of 20-50% with a tensile strength of about 3500 psi. These materials have good adhesion to vinyl, urethane and polycarbonate substrates as well as to natural fibers.

EXAMPLE 7

This example is not representative of the present invention. The procedure of Example 6 is followed with a coating composition similar to Example 1 with the single exception that Uvinul 400, i.e., 2,4 dihydroxybenzophenone, was used in place of the N-35 ultra-violet absorber. The curing rate is 40/ft/min/2 lamps. This speed is considered too slow for most commercial applications.

EXAMPLE 8

This example is illustrative of forming the inventive coating based on PCP-200/IPDI/HEA oligomer. The procedure is the same as described in Example 1, except that 292 grams of PCP-200 is used replacing 356 grams of poly THF-650.

EXAMPLES 9-13

These examples are illustrative of curing the inventive composition under an electron beam. The composition of Examples 1 to 4 and 8 (with the photo-initiator omitted), and with the percentages of ultra-violet absorber as indicated in Table II. The coating compositions are applied to a thickness of 1-1.5 mils on each side of a sheet of PVC. One Mrad was sufficient to cure the coatings in all cases.

                  TABLE II                                                         ______________________________________                                         EXAMPLE           9      10     11   12   13                                   ______________________________________                                         ultra-violet absorber                                                          weight percent    3%     3%     3%   3%   3%                                   Coating Comp. of Example                                                                         1      2      3    4    8                                    ______________________________________                                    

EXAMPLE 14

This example is illustrative of forming the inventive coating composition based on the PCP/IPDI/HEA oligomer with hydroxyethyl 2-cyano-3,3-diphenyl acrylate as ultra-violet absorber.

The quantities of the following items are combined as indicated below:

    ______________________________________                                                          QUANTITY                                                      ITEM  NAME             (gms)      (mols)                                       ______________________________________                                         A     PCP-200          292        0.55                                         B     NP               173.3      1.56                                         C     B,DDA            121.7      0.61                                         D     IPDI             267        1.20                                         E     HEA              139        1.20                                         F     Hydroxyethyl 2-                                                                cyano-3,3'-diphenyl                                                            acrylate         30               3%                                     ______________________________________                                    

The same procedure and conditions described in Example 1 is used. At the end of reaction the material is formulated with Vicure 10 and DC-193 and is ready for coating application.

EXAMPLE 15

This example is illustrative of applying the inventive coating composition of Example 14 to a clear polyvinylchloride sheet.

The formulation described in Example 14 is doctored onto a transparent PVC glazing by a 3-mil Bird applicator. The coated PVC substrate was cured under the UV light at 50 ft/min/2 lamps under nitrogen. The weatherability of the coating was tested in a Weather-Ometer for 4 weeks.

EXAMPLE 16

This example is illustrative of applying the inventive coating composition of Example 14 to a sheet of polycarbonate. The procedure of Example 15 was followed with the single exception that a polycarbonate glazing replaced the PVC substrate. Similar results were obtained.

For adequate outdoor protection it was found that, after ultra-violet curing a 3 mil. film containing 1-3% N-35 or N-539 on one side of a commercial PVC glazing of 110 mil. thickness is weather-resistant after an exposure period of four weeks in a Weather-Ometer. FIG. 1 shows that the light transmission for coated PVC containing N-35 or N-539 remains constant while the light transmission for untreated PVC decreases and for coated PVC without ultra-violet absorbers decreases.

FIG. 2 shows that the PVC glazings without N-35 or N-539 exhibit yellowing. After 4 weeks in a Weather-Ometer the PVC had a yellowness index of over 70; the coated PVC containing no Uvinul over 50 and the coated PVC containing 1 or 2% of N-35 and N-539 showed no yellowness.

FIG. 3 shows that the light transmission diminishes only slightly with a decrease in thickness of the coating composition containing 3% of N-539 on one side of a coated PVC cured under ultra-violet light. Coatings of a thickness of 1.5 mils performed as well as 3 mil coatings. Coatings of 0.5 mils showed only a slight decrease in the percentage of light transmission.

FIG. 5 shows similar results for a PVC glazing coated on both sides with a coating composition containing N-539 cured by electron beam. The thickness of the coating on each side varied between 1 and 1.5 mils. The coating containing 1% of N-539 showed a greater decrease in light transmission than the coating containing 2.3% of N-539.

FIG. 4 shows the yellowness index for PVC glazing coated with a coating composition with 3% N-539 on one side of the sheet and cured under UV. Sheets with coatings of 0.5 mils showed a yellowness index of approximately 10; sheets with coatings of 1.5 mils and 3 mils showed little measureable yellowness.

FIG. 6 shows a stability against yellowness for a PVC glazing with a coating thickness of 1 to 1.5 mils on both sides of the glazing and cured by electron beam. Only the coating containing 1% of N-539 showed a slight yellowing. The coating containing 2.3% of N-539 showed no yellowness. FIG. 7 shows that hydroxyethyl-2-cyano-3,3'-diphenyl acrylate was as effective as N-35 under the same conditions. The coated polycarbonate glazing after 4 weeks accelerated aging in the Weather-Ometer remained as clear as the unexposed sample. No yellowing was observed.

Table III shows additional test results indicating that the coating composition gives a strong, stain-resistant, solvent-resistant and adhesive coating which is the same for the coating with and without the ultra-violet light absorbers. Thus ultra-violet absorbers in a radiation curable coating improve weathering to a surprising extent without a loss of other desirable properties.

                                      TABLE III                                    __________________________________________________________________________     PHYSICAL PROPERTIES OF THE WEATHER-RESISTANT COATING                                       Pencil                                      Dry and Wet                        Hardness                                                                             Impact Strength                                                                        Tabor Abrasion                                                                           Stain Resistance                                                                        Acetone    Adhesion, %                        ASTM  (NBS PS55-74)                                                                          (ASTM D1044-56)                                                                          DuPont Yellow                                                                           Resistance (ASTM                              D01.53.02                                                                            in.-lb. Wt.Loss,mg.                                                                              Stain, 30 Min.                                                                          (ASTM D-1308-57                                                                           D-3002-71)             __________________________________________________________________________     PVC Glazing (110 mils)                                                                      HB*   80     --        No Stain                                                                               No          --                     Plexiglas (100 mils)                                                                       H**   8       --        No Stain                                                                               No          --                     Lexan Glazing (57 mils)                                                                      3B***                                                                              208     --        No Stain                                                                               No          --                     Coating, no Uvinul,                                                            one mil film on PVC                                                                        HB    64-78   10 ± 4 No Stain                                                                               Resistant   10                     Coating Containing                                                             Uvinul N-539, one mil                                                          film on PVC HB    64-72   10 ± 4 No Stain                                                                               Resistant   10                     __________________________________________________________________________      HB = Midpoint                                                                  H = Soft                                                                       B = Hard                                                                 

Although the invention has been described in considerable detail with reference to certain preferred embodiments thereof, it will be understood that variations and modifications can be effected within the spirit and scope of the invention as described above and as defined in the appended claims. 

What is claimed is:
 1. A laminate comprising a planar sheet of clear polyvinyl chloride with a film coating 0.1 to 10 mils in thickness comprising an acryl urethane oligomer represented by the formula: ##STR8## wherein R¹ is hydrogen or methyl; Y is a divalent urethane residue and an acrylic ultra-violet light absorber of Formula IV: ##STR9## wherein R⁴ is alkyl or hydroxy alkylene.
 2. A radiation curable coating composition comprising:A. an oligomer of Formula I: ##STR10## wherein: R¹ is hydrogen or methyl; Y is a divalent urethane residue; B. an acrylic ultra-violet absorber of Formula IV: ##STR11## wherein R⁴ is alkyl or hydroxy alkylene.
 3. The coating composition of claim 2, further comprising a vinyl monomer selected from the group consisting of N-vinyl-2-pyrrolidone, acrylic acid esters and mixtures thereof.
 4. The coating composition of claim 2 further comprising an addition polymerization inhibitor present in an amount sufficient to avoid the auto-polymerization of the composition during storage.
 5. The coating composition of claim 4 wherein the addition polymerization inhibitor is present in an amount from 100-300 PPM weight percent based upon the weight of the composition.
 6. The coating composition of claim 2 further comprising a surfactant.
 7. The coating composition of claim 6 wherein the surfactant is present in an amount from 0.1 to 5 weight percent based upon the weight of the composition.
 8. The coating composition of claim 6 wherein the surfactant is a silicone surfactant.
 9. The coating composition of claim 3 wherein the weight ratio of oligomer to vinyl monomer is from 1:9 to 9:1.
 10. The coating composition of claim 2 further comprising a photo-initiator present in an amount sufficient to initiate the desired polymerization under the influence of the amount of actinic light energy absorbed.
 11. The coating composition of claim 10 wherein the photo-initiator is present in an amount from 0.01 to 5 weight percent based upon the weight of the composition.
 12. The coating composition of claim 2 wherein the acrylic ultra-violet light absorber is present in an amount from 0.5 to 3 weight percent based on the weight of the composition.
 13. A coating composition of claim 2 which is photopolymerizable in the presence of ultra-violet light to produce an adherent coating that is weather-resistant, flexible, scratch-resistant, stain-resistant, abrasion-resistant, and solvent-resistant, said coating composition consisting essentially of:A. an oligomer of Formula II: ##STR12## wherein: R₁ is hydrogen or methyl;R₂ is lower alkylene; R₃ is aliphatic or cycloaliphatic; X is --O-- or --NH--; n is an integer from 2 to 50 inclusive; B. N-vinyl-2-pyrrolidone; C. 1-4 butanedioldiacrylate; D. ethyl-2-cyano-3,3-diphenyl acrylate present in an amount from 0.5 to 3 weight percent based on the weight of the composition; E. a photo-initiator present in an amount from 0.01 to 5 weight percent based on the weight of the composition; F. an addition polymerization inhibitor present in an amount from 100-300 PPM based on the weight of the composition; G. a silicone surfactant present in an amount from 0.1 to 5 percent based on the weight of the composition,wherein the ratio A:B is from 1:3 to 3:1; and wherein the ratio A:C is from 1:3 to 3:1.
 14. A coating composition of claim 2 which is photopolymerizable in the presence of ultra-violet light to produce an adherent coating that is weather-resistant, flexible, scratch-resistant, stain-resistant, abrasion-resistant, and solvent-resistant, said coating composition consisting essentially of:A. an oligomer of Formula III: ##STR13## wherein: R¹ is hydrogen or methyl;R² is lower alkylene; R³ is aliphatic or cycloaliphatic;X is --O-- or --NH--; n is an integer from 2 to 50 inclusive; B. N-vinyl-2-pyrrolidone; C. 1-4 butanedioldiacrylate; D. ethyl-2-cyano-3,3-diphenyl acrylate present in an amount from 0.5 to 3 weight percent based on the weight of the composition; E. a photo-initiator present in an amount from 0.01 to 5 weight percent based on the weight of the composition; F. an addition polymerization inhibitor present in an amount from 100-300 PPM based on the weight of the composition; G. a silicone surfactant present in an amount from 0.1 to 5 percent based on the weight of the composition,wherein the ratio A:B is from 1:3 to 3:1; and wherein the ratio A:C is from 1:3 to 3:1.
 15. The radiation curable coating composition of claim 2 wherein said acrylic ultra-violet absorber is ethyl-2-cyano-3, 3-diphenyl acrylate present in an amount from 0.5 to 3 weight percent based on the weight of the coating composition.
 16. The radiation curable coating composition of claim 2, further comprising a photo-initiator present in an amount from 0.01 to 5 weight percent based on the weight of the coating composition.
 17. A coating composition of claim 2 which is photopolymerizable in the presence of ultra-violet light to produce an adherent coating that is weather-resistant, flexible, scratch-resistant, stain-resistant, abrasion-resistant, and solvent-resistant wherein said oligomer of Formula I is an acryl urethane of Formula III: ##STR14## wherein: R¹ is hydrogen or methyl;R² is lower alkylene; R³ is aliphatic or cycloaliphatic; X is --O-- or --NH--; n is an integer from 2 to 50 inclusiveand further comprising a photopolymerizable vinyl monomer selected from the group consisting of N-vinyl-2-pyrrolidone, acrylic acid esters and mixtures thereof; and a photo-initiator present in an amount from about 0.01 to 5 weight percent based on the weight of the composition.
 18. A coating composition of claim 2 which is photopolymerizable in the presence of ultra-violet light to produce an adherent coating that is weather-resistant, flexible, scratch-resistant, stain-resistant, abrasion-resistant, and solvent-resistant wherein said oligomer of Formula I, is an acryl urethane of Formula II: ##STR15## wherein: R¹ is hydrogen or methyl;R² is lower alkylene; R³ is aliphatic or cycloaliphatic; X is --O-- or --NH--; n is an integer from 2 to 50 inclusive;and further comprising a photpolymerizable vinyl monomer selected from the group consisting of N-vinyl-2-pyrrolidone, acrylic acid esters, and mixtures thereof; and a photo-initiator present in an amount from 0.01 to 5 weight percent based on the weight of the composition.
 19. A laminate comprising a planar sheet of polycarbonate with a film coating 0.1 to 10 mils in thickness comprising an acryl urethane oligomer represented by the formula: ##STR16## wherein R¹ is hydrogen or methyl; Y is a divalent urethane residue and an acrylic ultra-violet light absorber of Formula IV: ##STR17## wherein R⁴ is hydroxy alkylene. 